Assessment of color change and surface roughness in composite resins and teeth subjected to remineralizing agents
YILDIZ, Gökçe | ERTÜRK AVUNDUK, Ayşe Tuğba | ATILAN YAVUZ, Sevim | Cengiz Yanardag, Esra
Objective: This study was conducted to determine the color change and surface roughness of a nanohybrid, a microhybrid, an indirect composite resin and human central incisor teeth after the application of fluoride varnish (FV) and casein phosphopeptide- amorphous calcium phosphate (CPP-ACP). Materials-Methods: Twenty-four specimens were fabricated from each composite material (Nova Compo C, Gradia Direct, Solidex and teeth) by using a teflon mold (7 mm diameter and 2 mm thickness). Initial (T0) color measurements were made on the non-reflective white surface of the composite resin materials (Nova Compo C, Gradia Direct, Solidex) and teeth with a spectrophotometer (Vita Easyshade V) and initial surface roughness (Ra) values were measured with a mechanical contact profilometer (Mituto...
Enerji İçeceklerinin Nanohibrit ve Mikro-hibrit Rezin Kompozitlerin Renk Değişimi ve Yüzey Pürüzlülüğü Üzerindeki Etkileri
Effects of Energy Drinks on Color Stability and Surface Roughness of Nanohybrid and Micro-hybrid Resin Composites
YILDIZ, Gökçe | ERTÜRK AVUNDUK, Ayşe Tuğba | ATILAN YAVUZ, Sevim | Cengiz Yanardag, Esra
Amaç: Bu çalışmanın amacı enerji içeceklerinin nano-hibrit ve mikro-hibrit rezin kompozitlerin renk değişimi ve yüzey pürüzlülüğü üzerindeki etkilerini değerlendirmektir. Materyal Ve Metot: Her bir rezin kompozit [G-ænial Posterior (mikro-hibrit) ve Clearfil Majesty Esthetic (nano-hibrit)] için otuz numune hazırlandı. Örnekler 24 saat boyunca 37°C'de distile su içinde post-polimerize edildi. Başlangıç renk ve yüzey pürüzlülüğü (Ra) ölçümlerinin ardından, örnekler test edilen solüsyonlara göre rastgele üç gruba (n=10/grup) ayrıldı: Distile su (kontrol), Red Bull ve Burn. Numuneler 1 hafta boyunca enerji içeceği çözeltilerine daldırılmıştır. ΔE00 değerleri test prosedüründen önce ve sonra CIEDE2000 formülü kullanılarak bir spektrofotometre ile hesaplandı. Yüzey pürüzlülüğü ölçümleri te...
Investigation of Various Finishing/Polishing Procedures on Color Stability of Composite Resins
Atılan Yavuz, Sevim | Ergel, Duygu | Ertürk Avunduk, Ayşe Tuğba | Cengiz Yanardag, Esra
Aim e objective of this study was to assess the impact of various nishing and polishing systems on the color stability of composite resins treated with co ee. Material and Method Fi y samples of each of nanohybrid and supra-nanohybrid composite resin materials were prepared and each material was randomly divided into 5 groups (n=10): Group 1: Control group (mylar strip), Group 2: One Gloss (one step), Group 3: One Gloss + polishing paste, Group 4: So ex disk (multistep), Group 5: So ex disk + polishing paste. e samples were colored in co ee solution for 144 hours to simulate six months of co ee consumption a er polishing. e color of the samples before-a er staining was measured with a spectrophotometer and ∆E00 values were calculated. Results Material, polishing type and the interac...
A comparative study of polishing systems on optical properties and surface roughness of additively manufactured and conventional resin based composites
ayşe tuğba ertürk avunduk | sevim atılan yavuz | hande filiz | Cengiz Yanardag, Esra
This study aimed to compare polishing systems on color stability, surface roughness, and gloss of additively manufactured permanent and conventional resin composites. Totally 250 disc specimens (6 mm*2 mm) were prepared from resin-based materials [G-ænial Posterior (GP), Clearfil Majesty Esthetic (CME), SonicFill-2 (SF), Tescera (Tes), and Crowntec (CT)]. Following baseline color (ΔE00), gloss (GU), and surface roughness (Ra) measurements, the specimens were randomly divided into 5 groups (n= 10/group) according to polishing systems: Control (mylar strips); OneGloss; OneGloss + Platina Hi-Gloss; OptiDisc; and OptiDisc + Platina Hi-Gloss. Specimens were immersed in coffee for 144 h following polishing. ΔE00, GU, and Ra measurements were repeated. Atomic force microscopy images were taken in...
Farklı Bitim/polisaj Sistemlerinin Rezin Kompozitlerin Renklenmesi Üzerine Ekisinin Değerlendirilmesi
Ergel, Duygu | Atılan Yavuz | Ertürk Avunduk, Ayşe Tuğba | Cengiz Yanardag, Esra
AMAÇ: Bu çalışmanın amacı farklı bitim/polisaj sistemlerinin kahve ile renklendirilen kompozit rezinlerin renk stabilitesi üzerine olan etkilerinin değerlendirilmesidir. GEREÇ VE YÖNTEM: Nanohibrit ve supra-nanohibrit kompozit rezin materyallerinin her birinden teflon kalıp kullanılarak 6 mm çapında 2 mm derinliğinde 50 adet numune hazırlandı. Her materyal rastgele 5 gruba (n=10) ayrıldı: [Grup 1: Kontrol grubu (şeffaf band), Grup 2: One Gloss, Grup 3: One Gloss + Polisaj patı, Grup 4: Soflex disk, Grup 5: Soflex disk+Polisaj patı]. Numuneler, cila sonrası altı aylık kahve tüketimini taklit etmek amacıyla 144 saat boyunca kahve çözeltisinde renklendirildi. Spektrofotometre cihazı ( Vita Easyshade V) ile renklendirme öncesi/sonrası numunelerin renk değişim (∆E00) değerleri hesaplandı...
Farklı Polisaj Sistemlerinin Restoratif Materyallerin Renk Stabilitesi, Yüzey Pürüzlülüğü ve Parlaklığı Üzerine Etkisinin Değerlendirilmesi
Hande Filiz | Ayşe Tuğba Ertürk Avunduk | Cengiz Yanardag, Esra | Sevim Atılan Yavuz
Amaç: Beş farklı polisaj sisteminin restoratif materyallerin renk stabilitesi, yüzey pürüzlülüğü ve parlaklığı üzerine etksinin karşılaştırılarak değerlendirilmesidir. Yöntem: Her bir rezin kompozitten [mikro-hibrid rezin kompozit (G-ænial Posterior), bulk-fill rezin kompozit (SonicFill-2), indirekt rezin kompozit (Tescera)] 30 örnek olmak üzere toplam 150 disk şeklinde (6 mm çapında ve 2 mm kalınlığında) örnek hazırlandı. Örnekler 24 saat boyunca 37°C'de distile su içinde bekletildi. Başlangıç renk, yüzey pürüzlülüğü (Ra) ve parlaklık ölçümlerinin ardından örnekler, polisaj sistemlerine göre rastgele 5 gruba (n=10) ayrıldı: kontrol (şeffaf bant), tek aşamalı polisajsistemi (One- Gloss, Shofu), tek aşamalı polisajsistemi + polisaj patı (Platina Hi-Gloss, Prevest Denpro), çok a...